Struktur as-cast tinastainless steel austeniticcastings nyaeta austenite + carbide atanapi austenite + ferrite. perlakuan panas bisa ngaronjatkeun daya tahan korosi of austenitic castings stainless steel.
Kelas Sarimbag tina Austenitic Stainless Steel | ||||||||
| AISI | W-stoff | DIN | BS | SS | AFNOR | UNE / IHA | JIS | UNI |
| 304 | 1.4301 | X5 CrNi 18 9 | 304 S 15 | 2332 | Z 6 CN 18.09 | F.3551 | SUS 304 | X5CrNi18 10 |
| 305 | 1.4303 | X5 CrNi 18 12 | 305 S 19 | - | Z 8 CN 18.12 | - | SUS 305 | X8CrNi19 10 |
| 303 | 1.4305 | X12 CrNiS 18 8 | 303 S 21 | 2346 | Z 10 CNF 18.09 | F.3508 | SUS 303 | X10CrNiS 18 09 |
| 304L | 1.4306 | X2 CrNiS 18 9 | 304 S 12 | 2352 | Z 2 CN 18.10 | F.3503 | SUS 304L | X2CrNi18 11 |
| 301 | 1.4310 | X12 CrNi 17 7 | - | 2331 | Z 12 CN 17.07 | F.3517 | SUS 301 | X12CrNi17 07 |
| 304 | 1.4350 | X5 CrNi 18 9 | 304 S 31 | 2332 | Z 6 CN 18.09 | F.3551 | SUS 304 | X5CrNi18 10 |
| 304 | 1.4350 | X5 CrNi 18 9 | 304 S 31 | 2333 | Z 6 CN 18.09 | F.3551 | SUS 304 | X5CrNi18 10 |
| 304LN | 1.4311 | X2 CrNiN 18 10 | 304 S 62 | 2371 | Z 2 CN 18.10 | - | SUS 304 LN | - |
| 316 | 1.4401 | X5 CrNiMo 18 10 | 316 S 16 | 2347 | Z 6 CND 17.11 | F.3543 | SUS 316 | X5CrNiMo17 12 |
| 316L | 1.4404 | - | 316 S 12/13/14/22/24 | 2348 | Z 2 CND 17.13 | SUS316L | X2CrNiMo17 12 | |
| 316LN | 1.4429 | X2 CrNiMoN 18 13 | - | 2375 | Z 2 CND 17.13 | - | SUS 316 LN | - |
| 316L | 1.4435 | X2 CrNiMo 18 12 | 316 S 12/13/14/22/24 | 2353 | Z 2 CND 17.13 | - | SUS316L | X2CrNiMo17 12 |
| 316 | 1.4436 | - | 316 S 33 | 2343 | Z 6 CND18-12-03 | - | - | X8CrNiMo 17 13 |
| 317L | 1.4438 | X2 CrNiMo 18 16 | 317 S 12 | 2367 | Z 2 CND 19.15 | - | SUS 317 L | X2CrNiMo18 16 |
| 329 | 1.4460 | X3 CrNiMoN 27 5 2 | - | 2324 | Z5 CND 27.05.Az | F.3309 | SUS 329 J1 | - |
| 321 | 1.4541 | X10 CrNiTi 18 9 | 321 S 12 | 2337 | Z 6 CND 18.10 | F.3553 | SUS 321 | X6CrNiTi18 11 |
| 347 | 1.4550 | X10 CrNiNb 18 9 | 347 S 17 | 2338 | Z 6 CNNb 18.10 | F.3552 | SUS 347 | X6CrNiNb18 11 |
| 316Ti | 1.4571 | X10 CrNiMoTi 18 10 | 320 S 17 | 2350 | Z 6 CNDT 17.12 | F.3535 | - | X6CrNiMoTi 17 12 |
| 309 | 1.4828 | X15 CrNiSi 20 12 | 309 S 24 | - | Z 15 SSP 20.12 | - | SUH 309 | X16 CrNi 24 14 |
| 330 | 1.4864 | X12 NiCrSi 36 16 | - | - | Z 12 NCS 35.16 | - | SUH 330 | - |
1. Solusi Perlakuan Panas
Spésifikasi umum perlakuan panas solusi nyaéta: manaskeun casting ka 950 ° C - 1175 ° C sarta nempatkeun eta dina cai, minyak atawa hawa sanggeus pelestarian panas pikeun sakabéhna ngabubarkeun carbide dina stainless steel pikeun ménta struktur fase tunggal. Pilihan suhu solusi gumantung kana eusi karbon dina baja tuang. Nu leuwih luhur kandungan karbon, nu leuwih luhur suhu solusi solid diperlukeun.
Dina raraga ngurangan bédana suhu antara beungeut casting baja jeung inti salila prosés pemanasan, métode pemanasan solusi perlakuan stainless steel austenitic kudu preheated dina suhu low lajeng gancang dipanaskeun kana suhu solusi. Waktos nahan kedah ningkat saluyu sareng ketebalan témbok tuang na ningkat.
Médium cooling pikeun pengobatan solusi tiasa cai, minyak atanapi hawa, anu cai anu paling sering dianggo. cooling hawa ngan cocog pikeun castings baja ipis-walled.
Spésifikasi perlakuan padet solusi matak Austenitic stainless steel | |||
| Kelas di Cina | Sarua Kelas Luar Negeri | Suhu solusi / ℃ | Teu karasa / HBW |
| ZG03Cr18Ni10 | / | 1050 - 1100 | / |
| ZG0Cr18Ni9 | / | 1080 - 1130 | / |
| ZG1Cr18Ni9 | G-X15CrNi18 8 (Kelas Jérman) | 1050 - 1100 | 140 - 190 |
| ZGCr18Ni9Ti | 950 - 1050 | 125 - 180 | |
| ZGCr18Ni9Mo2Ti | X18H9M2 (Kelas Rusia) | 1000 - 1050 | 140 - 190 |
| ZG1Cr18Ni12Mo2Ti | X18H12M2 (Kelas Rusia) | 1100 - 1150 | / |
| ZGCr18Ni11B | X18H11B (Rusia Kelas) | 1100 - 1150 | / |
| ZG03Cr18Ni10 | CF-3 (Kelas AS) | 1040 - 1120 | / |
| ZG08Cr19Ni11Mo3 | CF-3M (Kelas AS) | 1040 - 1120 | 150 - 170 |
| ZG08Cr19Ni9 | CF-8 (Kelas AS) | 1040 - 1120 | 140 - 156 |
| ZG08Cr19Ni10Nb | CF-8C (Kelas AS) | 1065 - 1120 (Stabilisasi dina 870 - 900) | 149 |
| ZG07Cr19Ni10Mo3 | CF-8M (Kelas AS) | 1065 - 1120 | 156 - 210 |
| ZG16Cr19Ni10 | CF-16F (Kelas AS) | 1095 - 1150 | 150 |
| ZG2Cr19Ni9 | CF-20 (Kelas AS) | 1095 - 1150 | 163 |
| ZGCr19Ni11Mo4 | CG-8M (Kelas AS) | 1040 - 1120 | 176 |
| ZGCr24Ni13 | 1095 - 1150 | 190 | |
| ZG1Cr24Ni20Mo2Cu3 | 1100 - 1150 | / | |
| ZG2Cr15Ni20 | CK-20 (Kelas AS) | 1095 - 1175 | 144 |
| ZGCr20Ni29Mo3Cu3 | CH-7M (Kelas AS) | 1120 | 130 |
| ZG1Cr17Mn13N | 1100 | 223 - 235 | |
| ZG1Cr17Mn13Mo2CuN | 1100 | / | |
| ZG0Cr17Mn13Mo2CuN | 1100 | 223 - 248 | |
2. Stabilisasi
stainless steel Austenitic boga résistansi korosi alus teuing sanggeus perlakuan solusi. Sanajan kitu, nalika casting ieu reheated ka 500 ° C-850 ° C atawa casting jalan dina rentang suhu ieu, kromium carbide bakal ulang endapanana sapanjang wates sisikian austenite, ngabalukarkeun korosi wates sisikian atawa weld cracking. fenomena ieu disebut sensitization. Dina raraga ngaronjatkeun daya tahan korosi intergranular of castings stainless steel austenitic misalna, éta umumna diperlukeun pikeun nambahkeun elemen alloying kayaning titanium na niobium. Sanggeus perlakuan solusi, reheat ka 850 ° C - 930 ° C, lajeng gancang tiis. Ku cara kieu, karbida titanium sareng niobium mimiti diendapkeun tina austenit, ku kituna nyegah présipitasi kromium karbida sareng ningkatkeun résistansi korosi wates sisikian tina stainless steel.
waktos pos: Aug-18-2021